Black Oxide Coating

The Basics of Black Oxide

By: Rick Delawder
as seen in the American Fastener Journal
Black oxide is unlike any other finish. No other process produces the same finish and combination of properties for less cost. Black oxide has certain properties and characteristics that makes it ideal for certain applications.

What is it?

Black oxide is a conversion coating formed by a chemical reaction produced when parts are immersed in the alkaline aqueous salt solution operated at approximately 285 degrees F. The reaction between the iron of the ferrous alloy and the hot oxide bath produces a magnitite (Fe3 O4) on the actual surface of the part. It is possible to oxidize non-ferrous metals under suitable conditions to form black oxides. It is possible to apply black oxide at room temperature, however it is not possible to achieve all of the benefits available from the "hot" oxide process. The cold black oxide process routinely shows color variation from part to part and the black material frequently rubs off in your hands. The cold process does not meet military or automotive specifications. Therefore the remainder of this article addresses the "hot" black oxide process.

How is the process performed?
The five basic steps for the black oxide conversion coating are clean; rinse; black oxide; rinse; supplementary coating (after-finish). If rust or scale is present on the part, additional steps such as acid pickling or alkaline de-scaling may have to be added before oxiding. Neutralizing and/or further rinsing may be necessary on assemblies and parts with blind holes to eliminate "flowering" or bleed-out. Black oxide cannot be produced over plated parts (zinc, nickel, chromium, cadmium, phosphate). This plating must be stripped prior to the black oxide process.

The supplementary coating (after-finish) will dictate the final appearance and function of the part. When a print or drawing specifies "Black Oxide" without any specific after-finish, it is interpreted as Black Oxide and Oil. It is recommended that an after-finish is always applied, as black oxide without an after-finish has very poor corrosion protection. However, with an oil, wax, or lacquer, it is possible to achieve excellent indoor corrosion protection (100+ hrs. in a humidity cabinet). Black oxides on steel are not suitable for severe outdoor applications or corrosive environments, but they can provide superior humidity cabinet results with proper supplementary coating. Black Oxides on Stainless steel and/or brass alloys will yield excellent corrosion protection, primarily due to their inherent properties.

The after-finish is usually determined by the part configuration and the end-use. If a "dry-to-touch" finish is needed, it is important to specify either Oil spin dry to touch, wax or lacquer. The oil after-finish will generally be a glossy finish, whereas the wax will be more matte. It is possible to use a torque/tension wax to provide added lubricity and reduced drive torque.

In order to determine the appropriate after-finish, you must first evaluate which after-finish to use. The following factors should be considered:

  • Length of protection required
  • Desired finished appearance (gloss/matte)
  • Storage conditions (humidity, vapor, temperature)
  • Final application
Test Procedures
Visual Test - The black oxide coating shall exhibit a satisfactory appearance. The black oxide coating shall cover the basis metal completely and shall be a uniform shade of black. The part shall show no evidence of pitting, intergranular attack, or etching. Please note: Black oxide does not exhibit a smoothing effect like plating or painting. Pre-existing scratches, tool marks, pits, scribe lines, and other surface defects will be visible after finishing (although they will be black).

Smut Test - Smut is a black or dark-colored, powdery residue, which comes off on the hand when rubbed. such tests shall be performed prior to the application of the after-finish.

Relative Humidity Test - Testing per ASTM D 2247, Standard Practice for Testing Water Resistance of Coatings in 100% Relative Humidity.

Read electro-mechanical engineering blog
You might also like
Black coating on steel
Black coating on steel
7 3 15 .. Metal Finishing : Hot Black Oxide Finish on
7 3 15 .. Metal Finishing : Hot Black Oxide Finish on ...
Black Python Gripper 118 Kg with Black Oxide Gun Coating
Black Python Gripper 118 Kg with Black Oxide Gun Coating ...
Raw Products Corp 18-8 Stainless Steel Black Oxide Button Socket Head Screws - 1/4-20 x 1/2" (FT) Qty-100
BISS (Raw Products Corp)
  • 18-8 Stainless Steel with Black Oxide Finish.
  • Black oxide provides corrosion protection to prevent rusting.
  • These fasteners are chemically treated to create the back oxide finish and are finished with wax.
  • A button socket cap screws head driven with a Allen key or Allen socket wrench, �#4-40 button socket cap screws black oxide stainless steel fasteners are clean heads...
  • A button socket cap screw, also known as a button socket head cap screw, socket screw or Allen button socket bolt, is a type of cap screw with a cylindrical head...
Milwaukee Milwaukee 48-89-2800 14 Piece Thunderbolt Black Oxide Drill Bit Set
Home Improvement (Milwaukee)
  • Thunderbolt Web, Provides Longer Life and Faster Driller Times
  • Parabolic Flute, Clears Chips Faster
  • 135 degree Split Point, Precision Start No Walking
  • 3-Flat Secure Grip Shank, Reduces Bit Slipping in Chuck
ASMC Industrial 1/4"-20 x 1 1/4" (FT) Coarse Thread Grade 5 Carriage Bolt Medium Carbon Steel Black Oxide Pk 50
BISS (ASMC Industrial)
  • Please see the specifications in the table above for full details. If you have any questions or doubts, or if your requirements include specific dimensions, please...
  • PICTURES ARE REPRESENTATIVE OF ITEM, BUT ARE NOT OF THE ACTUAL ITEM. Product dimensions, finish, head markings, thread length, stamping shape or forging shape, etc...
  • All ASMC Industrial fasteners are guaranteed to be of the highest quality.
  • All ASMC Industrial fasteners are fully traceable and lot-controlled.
Morton Machine Works Morton HDW-2 Black Oxide Steel Heavy Duty Flat Washer, 5/16" Bolt Size, 11/32" ID x 3/4" OD, 3/16" Thick (Pack of 10)
BISS (Morton Machine Works)
  • Heavy duty machined flat washer
  • Made of case hardened steel
  • Black oxide finish
  • Extra thick for increased strength
  • RoHs compliant
Related Posts